Himiki düzümi:
2205 poslamaýan polatdan ýasalan turba himiki düzümi
| Cr | Ni | Mo | Co | Nb (+ Ta) | Ti | V | W | Cu | C | Mn | N | Si | P | S | Fe | Al | |
| Min | 22.00 | 4.50 | 3.00 | 0.14 | 0.20 | ||||||||||||
| Maks | 23.00 | 6.50 | 3.50 | 0.03 | 0.20 | 0.70 | 0.03 | 0.02 | Bal |
Mehaniki aýratynlyklary:
2205 poslamaýan polatdan ýasalan turba himiki düzümi
| 0,2% subutnama stres | 450 N / mm2 | 65ksi |
| Dartyş güýji | 655 N / mm2 | 95ksi |
| Uzalma, 5.65√S0 | 25% | |
| Meýdany azaltmak | 45% | |
| Gatylyk (Brinell) | <270 | |
| Täsir güýji (otag synagy) | 80J (aw) | |
| Täsir güýji (-46 ° C): Uzynlyk | <100mm 80J | |
| 100-260mm 45J (35J min) | ||
| > 260mm Diňe maglumat üçin | ||
| Täsir güýji (-46oC): Transvers | 50-260mm 45J (35J min) | |
| > 260mm Diňe maglumat üçin | ||
Bellikler:
2205 poslamaýan polatdan ýasalan turba himiki düzümi
- Synag ASTM A370 ýa-da EN ISO 6892-1 (dartyş), EN ISO 6506-1 (gatylyk) laýyklykda geçiriler.
- Iň pes häsiýetler getirildi (otag temperaturasynda uzynlyk ugrunda synag edildi)
- Heatylylygy bejermek partiýasy üçin materialyň her eremeginde synag
- Gatylyk NACE MR 1075 laýyklykda bolmaly
- ASTM G48A poslama synagy (25 ° C) Çukur ýok we <3.0g / m2horlanmak
- Ferrit mazmuny 40-55%
- Dänäniň araçäk karbidlerinden, sigma, çaý we lava fazalaryndan erkin tassyklanan mikrostruktura
Fiziki aýratynlyklary: 2205 poslamaýan polatdan ýasalan turba himiki düzümi
| Dykyzlygy (Kg / m)3) | 7810 |
| Magnit geçirijiligi (20 ° C) | <50 |
| Youngaşlaryň moduly (kN / mm2) | 190 |
| Electricörite elektrik garşylygy, 20 ° C (µΩ.m) | 0.85 |
| Malylylyk giňelişiniň ortaça koeffisiýenti, 20-300 ° C (m / m /oC) | 11 x 10-6 |
| Aýratyn ýylylyk, 20 ° C (J / kg.K) | 400 |
| Malylylyk geçirijiligi, 20 ° C (W / mK) |